Taymaz TabariMehdi EbadiDheerendra SinghBasar CaglarM. Baris Yagci2025-10-0620180925-838810.1016/j.jallcom.2018.03.396http://dx.doi.org/10.1016/j.jallcom.2018.03.396https://gcris.yasar.edu.tr/handle/123456789/7876The photoelectrochemical activity of PbTiO3 (PTO) for water splitting was studied by linear sweeping voltammetry (LSV) and electrochemical impedance spectroscopy (EIS) techniques. The nanohydrolytic sol-gel method was used to synthesise a crystalline PbTiO3 perovskite nanoparticles. The physical and chemical properties of nanoparticles such as crystal structure surface area reducibility band gap energy particle morphology and size surface composition and valence states were investigated by X-Ray diffraction (XRD) BET temperature-programmed reduction (TPR) UV diffuse reflectance spectroscopy (UV-DRS) high resolution scanning and transmission electron microscopy (HR-SEM and HR-TEM) along with X-Ray photoelectron spectroscopy (XPS) and ultraviolet photoelectron spectroscopy (UPS). PTO nanoparticles showed pure crystallinity high surface area (14 m(2)/g) and high oxygen mobility. PTO has band gap energy of 2.66 eV which makes it active under visible light irradiation. Moreover nanoparticles vary in size and create a core-shell structure in a way that small particles surround large particles. The core-shell structure along with a free defected sites on the surface results in high photoelectrochemical activity for water splitting reaction. The I-V curve revealed that the PTO nanoparticles are a p-type electrode with the photocurrent efficiency of approximate to 19%. This suggests that the photoelectrode does not require external bias to initiate the water splitting and the reaction can be initiated simply by making a connection between the anode and the cathode. In addition a great stability is observed for PTO electrodes during the reaction as evidenced by no leaching to the reaction medium. (C) 2018 Elsevier B.V. All rights reserved.EnglishNonhydrolytic sol-gel, Photoelectrochemical activity, Perovskite, P-type electrode, Visible light activeCOMPOSITE THIN-FILMS, VISIBLE-LIGHT, PHOTOCATALYTIC ACTIVITY, HYDROTHERMAL SYNTHESIS, CHARGE SEPARATION, NANOTUBE ARRAYS, ZNO NANORODS, DOPED PBTIO3, FABRICATION, DEGRADATIONArticle